Now the tempered glass(toughened glass) have been widely used in different field, but its inherent properties – spontaneous explosion, bring the users troubles when it is occurred, and made it not so safety to a certain extent. How to reduce the spontaneous explosion rate of tempered glass? Followed suggestions could be your choice.
First, to choose the high quality float glass. The stones, bubbles, impurity substance, nickel sulfide is less in the high quality float glass, choose this kind float glass could reduce the spontaneous explosion rate greatly.
Second, to improve the processing quality for edges of the toughened glass, to avoid the scratches and bumping on tempered glass surface and edges. The polished edges is not only reduced the self-explosion, but also bring the aesthetic.
Third, to improve the degree of homogeneity for the stress on tempered glass surface and the symmetry along the direction of tempered glass thickness. This need the production line to improve its production technology.
Fourth, to use the heat soaked test after tempering process. To make the spontaneous explosion in advance, then after installation, the spontaneous explosion will be less.
Fifth, to use semi-tempered glass(heat strengthened glass) and laminated glass to replace the tempered glass. Less toughened glass used, then the rate of spontaneous explosion will be lower.
Sixth, to decrease the specification of tempered glass. The larger size for the toughened glass, the thicker for the tempered glass, the rate of spontaneous explosion will be higher. If the toughened glass is larger enough, the spontaneous explosion is unavoidable.
Seventh, to reduce the assembly stress on the tempered glass. The curvature for the toughened glass should be limited in the application, especially for the large size tempered glass, to avoid the self-explosion after long using under high stress from hardware.